YJS-535 high hardness rtv2 silikon for grc molding
Category: Grc&Gfrc Molding silicone  Publish Time: 2018-08-07 11:07 
YJS-535 is a type of hard silicone with hardness Shore A 35.It is widely used for making molds for artificial stone, gypsum casting, grc, grfc, cement/concrete decorative products and etc.
1. Description
YJS-535 is a type of hard silicone with hardness Shore A 35.  It is a kind of of two- component materials consisting of a flowable part A which when mixed with the curing agent or catalyst,cures at room temperature by a condensation reaction. It is widely used for making molds for artificial stone, gypsum casting, grc, grfc, cement/concrete decorative products and etc.

2. Features
-Amazing fluidity and easy to operate
-Complex design available
-Not Oily
-Stable quality, non-toxic and odorless catalyst provided
-Easy de-molding
-Excellent tension and tear strength
-High performance in duplication
-Shrinkage is almost zero (below 0.2)
-Excellent resistance to weather, temperature, aging, acid and aging-proofing.

3.Technical datasheet
Typical general characteristics
Inspection Method
Value
Product data (Catalyzed A+B)
YJS-535
Hardness
Shore A
35±2
Mix Ratio
A:B
100:2
Color
/
White
Pot life
25 ℃ (77F)
30-40mins
Curing time
25 ℃ (77F)
3-4 hours
Mixed viscosity
mPa.s
25000±2000
Tear-strength
kg/cm
25±2
Tensile-strength
M.pa
≥4.1
Elongation
%
 ≥420%
Shrinkage
%
≤0.2%

4. Using instructions
Step 1: Prepare and clean the prototype.
You must make sure your original molds perfect. fix the original mold on a board , then using some assistant material(like cardpaper) to make a frame for to surround the prototype. The frame is no need ,if we make the mold by brushing way .
 
 Step 2: Take the silicone and catalyst as the ratio 100:2 (silicone:catalyst=100:2) ,mix the silicone rubber and catalyst evenly. 
*Notes: Molding silicon rubber is a kind of flowing liquid and it contains two parts. Part A is a kind of flowing liquid and part B is the curing agent. Remember to mix part A and part B evenly, otherwise the silicon rubber will be partly solidified and this will bring troubles for your final operation. What’s more, the finished molds will have a short life. All of these will cause a waste of silicon rubber.
 
Step 3: Vacuum pumping
After mixed the silicone evenly, it is better to release the bubble by Vacuum pumping.
Step 4: Pouring cast or brushing cast
After released the bubble, we can pour/brush the silicone rubber on the prototype 
*Notes:Please finished all the steped within the operation time .If not it will cause cross linking reaction, and no more further steps will be available.So,we have to pay attention to the pot life and curing time.

5.Appearance
Part A: Silicone rubber is a white liquid
Part B: Catalyst is a non-toxic and odorless liquid, white transparent color.
ATT: We can provide fast/medium/slow catalyst of for hot, warm or cold season.

6.SHELF LIFE:
When stored at or below 32°C (89.6°F) in the original unopened containers, YJS-5 series Silicone Base and its Curing Agents have a usable life of 12 months.

7.Package
Silicone base:1kg/drum; 20kg/drum;25kg/drum;200kg/drum.
Curing Agent: 30g/bottle; 1kg/bottle